grade | tensile strength | Elongation at break | Yield Point | density | Maximum temperature | tensile modulus |
---|---|---|---|---|---|---|
AZ91D magnesium alloy | 230 MPa | 3.0 % | 150 MPa | 1.81 g/c㎡ | 595 °C | 44.8 GPa |
AZ80A magnesium alloy | 290 MPa | 2~5.0 % | 179 MPa | 1.81 g/c㎡ | 595 °C | 45 GPa |
AZ31B magnesium alloy | 280 MPa | 8 % | 160 MPa | 1.76 g/c㎡ | 596 °C | 46 GPa |
ZK61B magnesium alloy | 330 MPa | 12 % | 178 MPa | 1.81 g/c㎡ | 630 °C | 47GPa |
AZ61B magnesium alloy | 280 MPa | 14 % | 165 MPa | 1.81 g/c㎡ | 653 °C | 45 GPa |
AM60B magnesium alloy | 221 MPa | 4.0 % | 131 MPa | 1.81 g/c㎡ | 482 °C | 44.8 GPa |
grade | tensile strength | Elongation at break | Hardness | density | Maximum temperature |
---|---|---|---|---|---|
6061-T6 aluminum alloy | 2.46 kgf/cm² | 12.50% | B95 | 2.768 g/cm² | 1080° F |
7075-T6 aluminum | 4.78 kgf/cm² | 11% | B86 | 2.768 g/cm² | 380° F |
5052 aluminum | 1.62 kgf/cm² | 8 % | B60 | 2.768 g/c㎡ | 300° F |
6063 aluminum | 1.19 kgf/cm² | 11% | B55 | 2.768 g/c㎡ | 212° F |
MIC6 aluminum | 1.68 kgf/cm² | 3 % | B65 | 2.768 g/c㎡ | 1200° F |
grade | tensile strength | Elongation at break | Yield Point | density | Maximum temperature | tensile modulus |
---|---|---|---|---|---|---|
303 Stainless steel | 620 MPa | 50% | 140 MPa | 8 g/cm3 | 1420 °C | 193 GPa |
304 Stainless steel | 505 MPa | 70% | 215 MPa | 8 g/cm3 | 1455 °C | 193 GPa |
A316L Stainless steel | 560 MPa | 50% | 290 MPa | 8 g/cm3 | 925 °C | 193 GPa |
410S Stainless steel | 1475 MPa | 11% | 1005 MPa | 7.8 g/cm | 815 °C | 200 GPa |
416Stainless steel | 760 MPa | 22.5% | 585 MPa | 7.8 g/cm3 | 760 °C | 200 GPa |
We are equipped with advanced 3-axis, 4-axis and 5-axis CNC machining centers, including Haas, Jingdiao and other high-speed CNC milling machines. We can handle a wide variety of magnesium and aluminum milling projects that require high precision and complex shape machining parts, with extremely tight tolerances and excellent surface finishes.
Most processing type | Minimum Wall Thickness | Minimum end mill size | Minimum drill size | Maximum part size | Undercut | Radius:Depth |
---|---|---|---|---|---|---|
Three-axis machining | 1mm | 1mm x 2mm x 2mm | 0.5mm | 1100mm x 800mm x 650mm [x,y,z] | Square outline, full radius, dovetail outline | Machining tolerance is +/- 0.01mm. It is recommended that all areas of the part should be thicker than 0.51mm |
Four-axis machining | 1mm | 1mm x 2mm x 2mm | 0.5mm | 550mm x 350mm x 200mm [x,y,z] | Square outline, full radius, dovetail outline | Machining tolerance is +/- 0.01mm. It is recommended that all areas of the part should be thicker than 0.51mm |
Five-axis machining | 1mm | 1mm x 2mm x 2mm | 0.5mm | 550mm x 350mm x 200mm [x,y,z] | Square outline, full radius, dovetail outline | Machining tolerance is +/- 0.01mm. It is recommended that all areas of the part should be thicker than 0.51mm |
Most processing type | Maximum size | Minimum size diameter | Length | Wall thickness | Angle |
---|---|---|---|---|---|
cnc turning | 260mm*1100mm | 0.1mm | 0.2mm | 0.25mm | 30° |
Processing Type | smooth | Semi-gloss | matte | Textured |
---|---|---|---|---|
Precision Die Casting | A grade finish is made with a diamond polishing process that produces a shiny finish on injection molded parts. | Grade B finishes use coarse sandpaper to produce rougher parts than Grade A parts. Custom-molded plastic parts with a B-grade finish have a matte surface texture. | Grade C finishes use coarse grit to create a rough, uneven surface. C-finished injection molded parts have a matte surface texture. | Grade D finishes use grit and dried glass beads or oxides to create a very rough textured finish. Depending on the type of material used, the product can have a satin or matte finish. |